Data underpinning - Demonstration of high performance in a perovskite oxide supported solid oxide fuel cell based on La and Ca co-doped SrTiO3

Dataset

Associated persons

Associated organisations

Description

Perovskite electrodes have been considered as an alternative to Ni-YSZ cermet-based anodes as they afford better tolerance towards coking and impurities and due to redox stability can allow very high levels of fuel utilisation. Unfortunately performance levels have rarely been sufficient, especially for a second generation anode supported concept. A-site deficient lanthanum and calcium co-doped SrTiO3, La0.2Sr0.25Ca0.45TiO3 (LSCTA-) shows promising thermal, mechanical and electrical properties and has been investigated in this study as a potential anode support material for SOFCs. Flat multilayer ceramics cells were fabricated by aqueous tape casting and co-sintering, comprising a 450-m thick porous LSCTA- scaffold support, a dense YSZ electrolyte and a thin layer of La0.8Sr0.2CoO3-δ (LSC)-La0.8Sr0.2FeO3-δ ( LSF)-YSZ cathode. Impregnation of a small content of Ni significantly enhanced fuel cell performance over naked LSCTA-. Use of ceria as a co-catalyst was found to improve the microstructure and stability of impregnated Ni and this in combination with the catalytic enhancement from ceria significantly improved performance over Ni impregnation alone. With addition of CeO2 and Ni to a titanate scaffold anode that had been pre-reduced at 1000oC, a maximum powder density of 0.96Wcm-2 can be achieved at 800oC using humidified hydrogen as fuel. The encouraging results show that an oxide anode material, LSCTA- can be used as anode support with YSZ electrolyte heralding a new option for SOFC development.
Date made available4 Jul 2016
PublisherUniversity of St Andrews
Date of data production2012 - 2013

    Keywords

  • solid oxide fuel cell, perovskite, anode, electrochemistry

Discover related content
Find related publications, people, projects and more using interactive charts.

View graph of relations

ID: 244013149

Top